Tutor 1
Lamus Baez, Fabián Agusto
Resumen
En este trabajo de grado se estudió la influencia de la adición de fibras cortas en una matriz compuesta por caucho de neumático pulverizado y resina de poliol activado, mediante una evaluación experimental organizada en tres fases, en la primera fase se realizó el análisis de las propiedades físicas y mecánicas de la fibra de vidrio y de la fibra de fique individualmente con el fin de caracterizar la materia prima, posteriormente se identificó la adherencia de las fibras a la matriz mediante ensayos de PUL-OUT, en los cuales se concluyó que la fibra de vidrio no presenta adherencia con la matriz y por ende se descarta su uso en el material estudiado, mientras que la fibra de fique se adhiere a la matriz siempre que tenga una longitud mayor a la crítica, que para el caso es de 10 mm, punto en el cual se obtuvo la mayor resistencia al arrancamiento. Finalmente, se evaluaron las propiedades mecánicas del material, realizando cinco series de ensayos con cuatro repeticiones cada una, variando la cuantía de fibra de fique desde 0% hasta 8%, cada dos unidades porcentuales (0%, 2%, 4%, 6% y 8%); en cuanto a la tracción y la compresión el contenido de fibra es inversamente proporcional a la resistencia del material, al ocasionar espacios entre la matriz, sin embargo para el primer caso se da un esfuerzo residual, producido por la unión de la fibra a las dos partes del material tras su rotura; por otro lado la fibra genera mayor resistencia a la flexión y al corte, para el primer ensayo se observa que la fibra se comporta como soporte y reacciona evitando desplazamientos, y en para el segundo el fique evita la rotura del material al mantener unidas las secciones de las probetas imponiendo la necesidad de fuerzas mayores para que se dé la falla.
Resumen en lengua extranjera 1
A study on the influence of the addition of short fibers in a composite by tire rubber powder and resin activated polyol, by an experimental evaluation organized in three phases, in the first phase were analysed physical properties and mechanical properties of fiber glass and fique fiber individually in order to characterize the raw material, later was studied the adhesion of the fibers to the matrix by PUL-OUT trials, in which it was concluded that fiberglass no adhesion with the matrix and therefore its use in the test material is discarded, while fique fiber adheres to the matrix whenever it has more than the critical length, which in this case is 10 mm, at which point the greatest resistance was obtained pullout. Finally, the mechanical properties of the material were evaluated, through five series of tests four repetitions, varying the amount of fique fiber from 0% to 8%, each two percentage units (0%, 2%, 4%, 6 % and 8%), the tensile and compression of the material was inversely proportional with fiber content, because vacuum produced between the matrix, however for the first case, it has a residual stress produced by bonding the fiber to the two parts of the material after break; on the other hand the fiber generates greater strength flexural and shear, for the first test shows that the fiber behaves as a support and reacts avoiding displacement and for the second, the fique fiber prevents breakage of the material to mantain together the sections of the specimens, producing the need for a higher force to generate failure.
Palabras clave
Neumáticos usados, Fibras cortas, Reciclaje, Resistencia
Tipo de documento
Trabajo de grado - Pregrado
Licencia Creative Commons
This work is licensed under a Creative Commons Attribution-Noncommercial-No Derivative Works 4.0 License.
Fecha de elaboración
2016
Programa académico
Ingeniería Civil
Facultad
Facultad de Ingeniería
Citación recomendada
Mendivelso Buitrago, P. C. (2016). Evaluación del uso de fibras cortas como refuerzo a una matriz de poliol y residuo de neumático pulverizado. Retrieved from https://ciencia.lasalle.edu.co/ing_civil/85
Publisher
Universidad de La Salle. Facultad de Ingeniería. Ingeniería Civil